Semiconductor components and systems having encapsulated through wire interconnects (TWI) and wafer level methods of fabrication

ABSTRACT

A semiconductor component includes a semiconductor substrate having a substrate contact, and a through wire interconnect (TWI) attached to the substrate contact. The through wire interconnect provides a multi level interconnect having contacts on opposing first and second sides of the semiconductor substrate. The through wire interconnect (TWI) includes a via through the substrate contact and the substrate, a wire in the via having a bonded connection with the substrate contact, a first contact on the wire proximate to the first side, and a second contact on the wire proximate to the second side. The through wire interconnect (TWI) also includes a polymer layer which partially encapsulates the through wire interconnect (TWI) while leaving the first contact exposed. The semiconductor component can be used to fabricate stacked-systems, module systems and test systems. A method for fabricating the semiconductor component can include a film assisted molding process for forming the polymer layer.

BACKGROUND

In semiconductor manufacture, packaging is the final operation thattransforms a semiconductor substrate into a functional semiconductorcomponent. Typically, the semiconductor substrate is in the form of asemiconductor die. Packaging provides protection for the semiconductorsubstrate, a signal transmission system for the integrated circuits onthe semiconductor substrate, and external connection points for thecomponent. In response to the demand for smaller, lighter and thinnerconsumer products, new semiconductor components and new packagingmethods are being developed. The new components include high pin countsingle die packages, such as fine ball grid array (FBGA) packages, andmulti dice packages, such as stacked packages and systems in a package(SIP).

The new packaging methods include wafer level packaging (WLP), stackingof multiple semiconductor dice, and 3D packaging. With wafer levelpackaging (WLP), all of the packaging operations are performed on asemiconductor wafer containing multiple identical semiconductorsubstrates. In addition, all of the interconnects for a semiconductorcomponent are located within the peripheral outline of the component.Following wafer level packaging (WLP), the semiconductor components aresingulated from the wafer into chip scale components. In general, waferlevel packaging (WLP) provides smaller components and low cost volumemanufacture.

With stacking, two or more semiconductor components are stacked andinterconnected into a stacked system. A signal transmission system for astacked system includes interconnects which electrically connectadjacent stacked components. In addition, the signal transmission systemmust provide terminal contacts for inputting and outputting signals intothe system. The signal transmission system for a 3D component includesinterconnects that are vertically integrated, and not necessarily planarto the major planar surfaces of the component. For example,interconnects in the form of through wafer conductive vias can providesignal paths between opposing planar surfaces of a semiconductorcomponent.

In general, new types of interconnects have been developed forimplementing signal transmission systems to and from the integratedcircuits contained on the components. These interconnects must satisfydemanding electrical requirements. For example, the interconnects mustbe capable of a high density configuration, with minimal signal pathlengths and minimal cross talk. The interconnects must also have theability to accommodate thermal mechanical stresses, and to provide powerdistribution with controlled impedance over a wide frequency range. Inaddition, the interconnects must be capable of reliable manufactureusing readily available, or easily modifiable, semiconductor assemblyequipment.

Various embodiments of through wire interconnects to be furtherdescribed are able to satisfy the above requirements. In addition, thethrough wire interconnects provide a signal transmission system with 3-Dintegration, and with contacts suitable for stacking multiplesemiconductor components, or for mounting semiconductor components to anext level substrate. Further, the through wire interconnects arecapable of volume manufacture in reliable configurations usingsemiconductor assembly equipment.

However, the foregoing examples of the related art and limitationsrelated therewith, are intended to be illustrative and not exclusive.Other limitations of the related art will become apparent to those ofskill in the art upon a reading of the specification and a study of thedrawings.

BRIEF DESCRIPTION OF THE DRAWINGS

Exemplary embodiments are illustrated in the referenced figures of thedrawings. It is intended that the embodiments and the figures disclosedherein are to be considered illustrative rather than limiting.

FIG. 1A is a schematic plan view of a semiconductor component havingthrough wire interconnects (TWI);

FIG. 1B is a schematic side elevation view of the semiconductorcomponent of FIG. 1A;

FIG. 1C is an enlarged schematic cross sectional view taken alongsection line 1C-1C of FIG. 1A illustrating a through wire interconnect(TWI) of the semiconductor component;

FIGS. 2A-2L are enlarged schematic cross sectional views of alternateembodiments of the through wire interconnect (TWI) shown in FIGS. 1A-1C;

FIG. 2M is an enlarged schematic plan view of an alternate embodiment ofthe through wire interconnects (TWI) shown in FIGS. 1A-1C;

FIGS. 2N-2O are enlarged schematic cross sectional views of alternateembodiments of the through wire interconnects (TWI) shown in FIGS.1A-1C;

FIG. 3A is a schematic side elevation view of a stacked systemfabricated using two of the semiconductor components of FIGS. 1A-1C in acircuit side to back side orientation;

FIG. 3B is a schematic side elevation view of a stacked systemfabricated using two of the semiconductor components of FIGS. 1A-1C in acircuit side to circuit side orientation;

FIG. 4A is a schematic plan view of an alternate embodimentsemiconductor component having through wire interconnects (TWI) withpolymer members;

FIG. 4B is a schematic side elevation view of the semiconductorcomponent of FIG. 4A;

FIG. 4C is an enlarged schematic cross sectional view taken along line4C-4C of FIG. 4A illustrating a through wire interconnect (TWI) of thesemiconductor component of FIG. 4A;

FIG. 4D is an enlarged schematic cross sectional view taken alongsection line 4D-4D of FIG. 4C illustrating an outer layer of the throughwire interconnect (TWI);

FIG. 4E is an enlarged schematic cross sectional view taken alongsection line 4E-4E of FIG. 4C illustrating the outer layer of thethrough wire interconnect (TWI);

FIG. 5 is a schematic side elevation view equivalent to FIG. 4C of analternate embodiment 2× semiconductor component encapsulated on opposingsides;

FIGS. 6A and 6B are schematic cross sectional views of a test systemincorporating the semiconductor component of FIGS. 4A-4E;

FIG. 7 is a schematic cross sectional view of an alternate embodimenttest system incorporating the semiconductor component of FIGS. 4A-4E;

FIG. 8 is a schematic cross sectional view of module systemincorporating the semiconductor component of FIG. 5;

FIG. 9A is a schematic plan view of a wafer system incorporatingmultiple semiconductor components of FIGS. 1A-1C bonded to asemiconductor wafer;

FIG. 9B is an enlarged schematic cross sectional view taken alongsection line 9B-9B of FIG. 9A illustrating a single semiconductorcomponent bonded to the semiconductor wafer;

FIG. 10 is a schematic side elevation view of a wafer to wafer systemincorporating semiconductor components having through wire interconnects(TWI);

FIGS. 11A-11D are schematic side elevation views illustrating steps in afilm assisted molding method for fabricating the semiconductor componentof FIGS. 1A-1C;

FIG. 12A is an enlarged schematic view taken along line 12A-12A of FIG.11A;

FIG. 12B is an enlarged schematic cross sectional view taken along line12B-12B of FIG. 11B;

FIG. 12C is an enlarged schematic view taken along line 12C-12C of FIG.11D;

FIGS. 13A-13B are schematic cross sectional views showing steps in amethod for fabricating the alternate embodiment semiconductor componentof FIGS. 4A-4E;

FIG. 14 is a schematic side elevation view equivalent to FIG. 1B of analternate embodiment semiconductor component encapsulated on six sides;

FIGS. 15A-15D are schematic cross sectional views showing steps in amethod for fabricating the alternate embodiment semiconductor componentof FIG. 2K;

FIGS. 16A-16C are schematic views showing steps in a method forfabricating an embodiment semiconductor component using a film frame.

DETAILED DESCRIPTION

As used herein, “semiconductor component” means an electronic elementthat includes a semiconductor substrate or makes contact with asemiconductor substrate. “Semiconductor substrate” means an electronicelement, such as a semiconductor die, or a semiconductor package thatincludes integrated circuits and semiconductor devices. “Interconnect”means an electrical element which electrically connects differentelectrical elements and transmits signals between these elements.“Wafer-level” means a process conducted on an element, such as asemiconductor wafer, containing multiple semiconductor components orsubstrates. “Die level” means a process conducted on a singulatedelement, such as a singulated semiconductor die or package. “Chip scale”means having an outline about the same as that of a semiconductor die.“Wafer size” means having an outline about the same as that of asemiconductor wafer.

Referring to FIGS. 1A-1C, a semiconductor component 10 (FIG. 1A) isillustrated. The semiconductor component 10 (FIG. 1A) includes asemiconductor substrate 12 (FIG. 1B); a plurality of through wireinterconnects 14 (FIG. 1B) on the semiconductor substrate 12; and apolymer layer 16 on the semiconductor substrate 12 encapsulating atleast a portion of each through wire interconnect 14. The semiconductorsubstrate 12 (FIG. 1B) can comprise a conventional semiconductor die, ora thinned semiconductor die, having integrated circuits 22 (FIG. 1C)constructed in a desired electrical configuration using activesemiconductor devices such as transistors. For example, thesemiconductor substrate 12 (FIG. 1B) can comprise a high speed digitallogic device, such as a dynamic random access memory (DRAM), a staticrandom access memory (SRAM), a flash memory, a microprocessor, a digitalsignal processor (DSP), an application specific integrated circuit(ASIC), an imager device, or a MEMS type device (e.g., accelerometer,microphone, speaker, electro mechanical device). In addition, thesemiconductor substrate 12 (FIG. 1B) can comprise a tested die that hasbeen certified as a known good die.

As shown in FIG. 1A, in the illustrative embodiment, the semiconductorsubstrate 12 is a generally rectangular shaped die having opposedlateral edges and opposed longitudinal edges. However, the semiconductorsubstrate 12 (FIG. 1A) can have any polygonal shape, such as square ortriangular, and can also have a circular or oval shape. In addition, thesemiconductor substrate 12 can comprise a full thickness semiconductordie or a thinned semiconductor die. As shown in FIG. 1C, thesemiconductor substrate 12 includes a circuit side 17 (“first side” insome of the claims), and a back side 18 (“second side” in some of theclaims).

As also shown in FIG. 1A, the semiconductor substrate 12 includes aplurality of substrate contacts 20 on the circuit side 17, which in theillustrative embodiment comprise the device bond pads. Alternately,rather than being the device bond pads, the substrate contacts 20 cancomprise redistribution contacts (i.e., contacts formed in conjunctionwith a redistribution layer (RDL)). In addition, the substrate contacts20 can comprise a highly-conductive, wire-bondable metal, such asaluminum or copper. The substrate contacts 20 can also comprise stacksof different metals, such as aluminum-nickel-gold,aluminum-nickel-solder, copper-palladium, and aluminum on copper.

As another alternative, at least some of the substrate contacts 20 (FIG.1A) can comprise special purpose contacts formed specifically forconstructing the through wire interconnects 14. For example, thesubstrate contacts 20 can comprise electrically isolated contacts, thatare not in electrical communication with the integrated circuits 22(FIG. 1C) on the semiconductor substrate 12. As will be furtherexplained, this concept can be employed in stacked components to reduceunwanted capacitance, noise, bleed off voltage and bleed off current.

For simplicity, the semiconductor substrate 12 (FIG. 1A) is illustratedwith only four substrate contacts 20 (FIG. 1A) arranged in a single row.However, in actual practice the semiconductor substrate 12 (FIG. 1A) caninclude tens of substrate contacts 20 (FIG. 1A) arranged in a desiredconfiguration, such as a center array, an edge array or an area array.Also in the illustrative embodiment, the substrate contacts 20 (FIG. 1A)have a generally rectangular peripheral outline and angled corners.However, as with the semiconductor substrate 12 (FIG. 1A), the substratecontacts 20 (FIG. 1A) can have any polygonal shape including square,circular, triangular and oval. In addition, a size of the substratecontacts 20 (FIG. 1C) can be selected as required. For example, eachsubstrate contact 20 (FIG. 1C) can have a length (L) (FIG. 1C) of fromabout 50 μm to 200 μm and a width (W) (FIG. 1C) of from about 50 μm to200 μm. Also in FIG. 1A, each substrate contact 20 has an associatedthrough wire interconnect 14. However, the through wire interconnects 14can also be formed on only selected substrate contacts 20. For example,only the substrate contacts 20 having a selected output or inputconfiguration (e.g., Vss, Vcc) can be equipped with a through wireinterconnect 14.

As shown in FIG. 1C, the substrate contacts 20 can be in electricalcommunication with internal conductors 24 located within thesemiconductor substrate 12 proximate to the circuit side 17. Inaddition, the internal conductors 24 are in electrical communicationwith the integrated circuits 22 in the semiconductor substrate 12. Theinternal conductors 24 (FIG. 1C) can be part of the internal structureof the semiconductor substrate 12, and can comprise a highly conductivemetal, such as aluminum or copper. Further, a die passivation layer 26(FIG. 1C) proximate to the circuit side 16 protects the internalconductors 24 (FIG. 1C) and the integrated circuits 22 (FIG. 1C). Thedie passivation layer 26 (FIG. 1C) can comprise an electricallyinsulating material, such as BPSG (borophosphosilicate glass), a polymeror an oxide. In addition, the die passivation layer 26 (FIG. 1C)includes openings 44 (FIG. 1C) aligned with the substrate contacts 20which provide access to the substrate contacts 20. All of the elementsof the semiconductor substrate 12 including the integrated circuits 22(FIG. 1C), the internal conductors 24 (FIG. 1C), and the die passivationlayer 26 (FIG. 1C), can be formed using well known semiconductorfabrication processes.

As also shown in FIG. 1C, the through wire interconnect 14 includes avia 28 through the substrate contact 20 and the semiconductor substrate12, a wire 30 in the via 28, a bonding member 32 on the wire 30 and thesubstrate contact 20, and a polymer material 36 in the via 28.

The via 28 (FIG. 1C) extends through the substrate contact 20, andthrough the full thickness of the semiconductor substrate 12, from thecircuit side 17 to the back side 18 thereof. In the illustrativeembodiment, the via 28 (FIG. 1C) is generally circular, and has aninside diameter (ID) which is about 1.5 to 3 times larger than theoutside diameter (OD) of the wire 30 (FIG. 1C). By way of example, thewire 30 (FIG. 1C) can have an outside diameter (OD) of about 25 μm, andthe via 28 (FIG. 1C) can have an inside diameter (ID) of about 37.5 μmto 75 μm. In addition, a length of the via 28 (FIG. 1C) is dependent onan overall thickness T of the semiconductor substrate 12 (FIG. 1C). Arepresentative range for the thickness T of the semiconductor substrate12 (FIG. 1C) can be from about 10 μm to 725 μm, depending on whether thesemiconductor substrate 12 is a thinned or a full thickness die orwafer.

The via 28 (FIG. 1C) can also include an insulating layer 34 (FIG. 1C)formed on an inside diameter thereof, which electrically insulates thevia 28 (FIG. 1C) from the integrated circuits 22 (FIG. 1C), and otherelectrical elements on the semiconductor substrate 12. The insulatinglayer 34 (FIG. 1C) can comprise an electrically insulating material,such as a polymer (e.g., polyimide or parylene) or an oxide (e.g.,SiO₂). Alternately, the wire 30 (FIG. 1C), rather than the via 28 (FIG.1C), or in addition to the via 28 (FIG. 1C), can be electricallyinsulated.

In FIG. 1A, the via 28 is illustrated as being located in an upper lefthand corner of the substrate contact 20. In other words, the via 28 isoffset in both x and y directions from a center of the substrate contact20. In this case, the via 28 can have an inside diameter (ID) (FIG. 1C)that is about one half of the width (L) (FIG. 1C) of the substratecontact 20 (FIG. 1C). Alternately, the via 28 can be located anywhere onthe substrate contact 20 such as in the center of the substrate contact20. Also, rather than just one via 28, the substrate contact 20 caninclude multiple vias 28.

As shown in FIG. 1C, the wire 30 is located along a longitudinal axis ofthe via 28, and extends across the entire length of the via 28. The wire30 (FIG. 1C) can be held in place in the via 28 (FIG. 1C) by the polymermaterial 36 (FIG. 1C), which fills the via 28 (FIG. 1C) and surroundsthe wire 30 (FIG. 1C). The polymer material 36 can comprise anelectrically insulating curable polymer, such as a polyimide, an epoxyor a silicone. Also, the polymer material 36 (FIG. 1C) can includefillers, such as silicates, configured to reduce the coefficient ofthermal expansion (CTE) and adjust the viscosity of the dielectricmaterial. Suitable curable polymers are manufactured by Shinitsu ofJapan, and Dexter Electronic Materials of Rocky Hill, Conn. For someapplications, the polymer material 36 can comprise an electricallyconductive material, such as a nano particle conductive polymer.

As also shown in FIG. 1C, the wire 30 (FIG. 1C) includes a loop portion50, and a first end 38 (FIG. 1C) extending out of the via 28 (FIG. 1C)and bonded to the substrate contact 20 (FIG. 1C). The wire 30 (FIG. 1C)also includes a second end 40 (FIG. 1C) proximate to the back side 18(FIG. 1C) of the semiconductor substrate 12. The through wireinterconnect 14 (FIG. 1C) also includes a bonded connection 42 (FIG. 1C)between the first end 38 (FIG. 1C) of the wire 30 and the substratecontact 20. In addition, the second end 40 (FIG. 1C) of the wire 30 cancomprise a second contact in the form of a generally spherically shapedcontact ball 46, such as a “free air ball” formed using an electronicflame off (EFO) process during the bonding process.

In the through wire interconnect 14 (FIG. 1C), the bonded connection 42(FIG. 1C) comprises a wedge bond formed using a ball bonding process,such as thermosonic or thermocompressive wire bonding. Alternately, abonded connection can comprise a wedge bond formed using ultrasonic wirebonding. As another alternative, the wire 30 can comprise a bondingribbon, and a bonded connection can comprise a ribbon wire bond. Asanother alternative, the wire 30 can comprise a compressed wire, and abonded connection can be in the form of a stud bump and a compressionflange on the compressed wire.

U.S. patent application Ser. No. 11/296,057 filed on Dec. 7, 2005,entitled “Semiconductor Components having Through Wire Interconnects(TWI), And Methods And Systems For Fabricating SemiconductorComponents”, which is incorporated herein by reference, describes methodand systems for fabricating semiconductor components with through wireinterconnects. U.S. patent application Ser. No. 11/102,408 filed on Apr.8, 2005 entitled “Method And System For Fabricating SemiconductorComponents With Through Wire Interconnects”, which is also incorporatedherein by reference, also describes methods and systems for fabricatingsemiconductor components with through wire interconnects.

A representative outside diameter (OD) (FIG. 1C) of the wire 30 can befrom about 12 μm to about 150 μm. In addition, the wire 30 (FIG. 1C) cancomprise a conventional wire material used in semiconductor packaging,such as solder alloys, gold, gold alloys, copper, copper alloys, silver,silver alloys, aluminum, aluminum-silicon alloys, and aluminum-magnesiumalloys. In addition, the wire 30 (FIG. 1C) can comprise a metal, or ametal alloy, that does not contain reductions of hazardous substances(ROHS), such as lead. Exemplary ROHS free metals include lead freesolders, such as 97.5% Sn2.5% Ag. Other ROHS free metals include gold,copper and alloys of these metals such as copper coated with a layer offlash gold. Also, the melting point of the wire 30 (FIG. 1C) shouldpreferably be greater than that of the substrate contact 20. Further,the wire 30 can comprise an insulated bonding wire having anelectrically insulating outer layer, such as a polymer. The insulatinglayer on the wire 30 can take the place of the insulating layers 34(FIG. 1C). This type of insulated bonding wire is available from MicroBond of Canada.

As also shown in FIG. 1A, in the through wire interconnect 14, thebonding member 32 is located next to the via 28, and is bonded to thesubstrate contact 20 in a right, lower quadrant of the substrate contact20. Alternately, the bonding member 32 (FIG. 1C) can be centered on thesubstrate contact 20 (FIG. 1C) and on the via 28 (FIG. 1C), or locatedon any portion of the substrate contact 20 (FIG. 1C) or the via 28 (FIG.1C).

The bonding member 32 (FIG. 1C) bonds the first end 38 of the wire 30(FIG. 1C) to the substrate contact 20 (FIG. 1C). In addition, thebonding member 32 (FIG. 1C) functions as a first contact for the throughwire interconnect, as a securing and supporting structure for the wire30 (FIG. 1C), and as a bonding structure for bonding the through wireinterconnect 14 (FIG. 1C) to an external electrical element, such ascontacts on a support substrate, or another through wire interconnect onanother semiconductor component. The bonding member 32 (FIG. 1C)preferably comprises a non oxidizing, bondable material such as gold orplatinum, or an easily reflowable material, such as solder.

In the illustrative embodiment, the bonding member 32 (FIG. 1C)comprises a stud bump, or a ball bump, bonded to the substrate contact20. In this case, the bonding member 32 (FIG. 1C) can be formed using awire bonder, a stud bumper, or a ball bumper. Alternately, the bondingmember 32 (FIG. 1C) can comprise a solder bump, a welded connection, ora conductive polymer connection. In FIG. 1C, the bonding member 32 has adiameter which is less than the length (L) and the width (W) of thesubstrate contact 20 (e.g., 25% to 75%), such that it covers only aportion of the substrate contact 20, and does not cover the via 28.However, a bonding member can also be configured to substantially coverthe substrate contact 20 and the via 28.

As shown in FIG. 1B, the polymer layer 16 substantially covers thecircuit side 17 of the substrate 12, and has a peripheral outlinematching that of the substrate 12. Alternately, the polymer layer 16 cancover only selected portions of the circuit side 17 of the substrate 12,such as only the areas surrounding the substrate contacts 20. As shownin FIG. 1C, the polymer layer 16 encapsulates the substrate contacts 20and loop portions 50 of the wires 30 of the through wire interconnects14. The polymer layer 16 also substantially encapsulates the bondingmember 32. However, a tip portion 48 of the bonding member 32 remainsunencapsulated by the polymer layer 16, and forms a first contact forthe through wire interconnect 14 proximate to the circuit side 17.

The polymer layer 16 (FIG. 1C) can comprise a curable polymer materialsuch as silicone, polyimide, epoxy parylene or a molding compound. Inaddition, these materials can include fillers, such as silicates,configured to reduce the coefficient of thermal expansion (CTE), andadjust the viscosity of the polymer material. One suitable curablepolymer material is manufactured by Dexter Electronic Materials of RockyHill, Conn. under the trademark “HYSOL” FP4450. One suitable moldingcompound is manufactured by JSR Micro of North America under the productdesignation JSR WPR-S17OP. Other molding compounds particularly suitedfor the film assisted molding process to be hereinafter described aremanufactured by Shin-Etsu Chemical Co. Ltd. of Japan.

The polymer layer 16 (FIG. 1C) has a planar surface which facilitatesstacking of the semiconductor component 10 (FIG. 1A) to anothercomponent, or to a next level substrate. In addition, the polymer layer16 (FIG. 1C) encapsulates the wire 30 (FIG. 1C), the loop portion 50(FIG. 1C) of the wire 30 (FIG. 1C), and the bonding member 32 (FIG. 1C).

Referring to FIGS. 2A-2O, alternate embodiment through wireinterconnects 14-1 to 14-15 are illustrated. The through wireinterconnects 14-1 to 14-15 are all substantially similar to the throughwire interconnect 14 (FIGS. 1A-1C).

In FIG. 2A, a through wire interconnect 14-1 includes a wire 30-1encapsulated by a polymer material 36-1, and a second contact 46-1 inthe form of a planar end of the wire 30-1. In addition, the polymermaterial 36-1 and the second contact 46-1 have a same planar surface.

In FIG. 2B, a through wire interconnect 14-2 includes a wire 30-2encapsulated by a polymer material 36-2, and a second contact 46-2 inthe form of a stud bump or a ball bump on the wire 30-2 and the polymermaterial 36-2.

In FIG. 2C, a through wire interconnect 14-3 includes a wire 30-3encapsulated by a polymer material 36-3, and a second contact 46-3 inthe form of a metal bump, such as solder, gold, or nickel on the end ofthe wire 30-1. In this embodiment the second contact 46-3 can comprise ameniscus solder coated end. Alternately, with the wire 30-3 comprisinggold, the second contact 46-3 can comprise nickel plated with a solderbump or ball.

In FIG. 2D, a through wire interconnect 14-4 includes a wire 30-4encapsulated by a polymer material 36-3 that is etched back to expose asecond contact 46-4 on the wire 30-4.

In FIG. 2E, a through wire interconnect 14-5 includes a wire 30-5encapsulated by a polymer material 36-5, and a second contact 46-5 inthe form of a planar metal pad on the wire 30-5 and the polymer material36-5.

In FIG. 2F, a through wire interconnect 14-6 includes a wire 30-6encapsulated by a polymer material 36-6. In addition, a substrate 12-6is etched back to expose the polymer material 36-6. Further, a secondcontact 46-6 comprises a planar end of the wire 30-6 and the polymermaterial 36-6 have a same planar surface.

In FIG. 2G, a through wire interconnect 14-7 includes a wire 30-7encapsulated by a polymer material 36-7. In addition, both the polymermaterial 36-7 and a back side of a substrate 12-7 are etched back toexpose a second contact 46-7 which comprises an end of the wire 30-7.

In FIG. 2H, a through wire interconnect 14-8 includes a wire 30-8encapsulated by a polymer material 36-8. However, the polymer material36-8 also encapsulates the circuit side of the substrate 12-8. In thisembodiment, the polymer material 36-8 takes the place of both thepolymer layer 16 (FIG. 1C) and the polymer material 36 (FIG. 1C). Aswill be further explained, the polymer material 36-8 can be formed usinga film assisted molding process. The through wire interconnect 14-8 alsoincludes a second contact 46-8 which comprises a planar end of the wire30-8, which is co-planar to the polymer material 36-8.

In FIG. 2I, a through wire interconnect 14-9 includes a wire 30-9encapsulated by a polymer material 36-9. As with the previousembodiment, the polymer material 36-9 also encapsulates the circuit sideof the substrate 12-9. The through wire interconnect 14-9 also includesa second contact 46-9 which comprises an end of the wire 30-9 projectingfrom a surface of the polymer material 36-9.

In FIG. 2J, a through wire interconnect 14-10 includes a wire 30-10encapsulated by a polymer material 36-10. As with the previousembodiment, the polymer material 36-10 also encapsulates the circuitside of the substrate 12-10. The through wire interconnect 14-10 alsoincludes a back side polymer layer 16-10, and a second contact 46-10which comprises a planar end of the wire 30-10 co-planar to the backside polymer layer 16-10.

In FIG. 2K, a through wire interconnect 14-11 includes a wire 30-11bonded to a tip portion of a bonding member 32-11. In this embodiment, abonded connection 42-11 is formed between the wire 30-11, and the tipportion of the bonding member 32-11. For example, the bonding member32-11 can comprise a stud bump bonded to the substrate contact 20-11,and the bonded connection 42-11 can comprise a ball bond formed on thestud bump. Alternately, the bonded connection 42-11 can be formedanywhere on the bonding member 32-11 such as in the center, or on anexterior surface thereof. A polymer layer 16-11 substantiallyencapsulates the through wire interconnect 14-11, but leaves the bondedconnection 42-11 and the tip portion of the bonding member 32-11 exposedas a first contact for the through wire interconnect 14-11. In addition,the polymer layer 16-11 also fills the via 28-11 and secures the wire30-11 therein, substantially as previously described for polymermaterial 36 (FIG. 1C). The polymer layer 16-11 can be formed using afilm assisted molding process to be hereinafter described.

In FIG. 2L, a through wire interconnect 14-12 includes a bonding member32-12 in the form of a double bump. In this embodiment, a bondedconnection 42-12 comprises a wire 30-12 within the bonding member 32-12sandwiched between the double bumps. Alternately, the bonded connection42-12 can be formed between the lowermost bump of the bonding member32-12 and the substrate contact 20-12. U.S. Pat. Nos. 5,496,775 and6,717,245, both of which are incorporated herein by reference, disclosedouble bump structures and techniques. A polymer layer 16-12substantially encapsulates the through wire interconnect 14-12, butleaves a portion of the bonding member 32-12 exposed as a first contactfor the through wire interconnect 14-12. In addition, the polymer layer16-12 also fills the via 28-12 and secures the wire 30-12 therein,substantially as previously described for polymer material 36 (FIG. 1C).The polymer layer 16-12 can be formed using a film assisted moldingprocess to be hereinafter described.

In FIG. 2M, through wire interconnects 14-13 include redistributionconductors 31-13 and pads 33-13 in electrical communication with thesubstrate contacts 20-13. The pads 33-13 can comprise test pads, wirebonding pads, outer lead bond OLB pads, or extended rdl pads. Inaddition, the through wire interconnects 14-13 include a polymer layer16-13, which has been cut away to show the redistribution conductors31-13 and pads 33-13. The polymer layer 16-13 also includes windows oropenings which provide access to the pads 33-13. The pads 33-13 permittemporary electrical connections to be made for performing testprocedures, such as functional, parametric and burn-in testing. Forexample, the integrated circuits 22 (FIG. 1C) on the semiconductorsubstrate 12 (FIG. 1C) can be tested or “probed” prior to fabrication orpartially fabrication of the through wire interconnects 16-13. Theredistribution conductors 31-13 and the pads 33-13 can have any desiredpattern, and can connect multiple through wire interconnects 14-13together substantially as shown in FIG. 2M. As also shown in FIG. 2M,some of the through wire interconnects 14-13 do not include anassociated pad 33-13.

In FIG. 2N, a through wire interconnect 14-14 includes a bondedconnection 42-14 in the form of a wedge bond formed between the wire30-14 and the substrate contact 20-14 using an ultra sonic or wedgebonding process. Alternately, the bonded connection 42-14 can comprise aball bond formed using a thermosonic or thermocompression bond. Inaddition, there is no bonding member 32 (FIG. 1C) on the bondedconnection 42-14. A polymer layer 16-14 encapsulates the through wireinterconnect 14-14, while leaving a tip portion 35-14 of the wire 30-14exposed as a first contact for the through wire interconnect 14-14. Thepolymer layer 16-14 also fills the via 28-14 and secures the wire 30-14therein, substantially as previously described for polymer material 36(FIG. 1C). As will be further explained, the tip portion 35-14 can alsoinclude a wear resistant or penetration enhancing layer. In addition,the polymer layer 16-14 can be formed using a film assisted moldingprocess to be hereinafter described.

In FIG. 2O, a through wire interconnect 14-15 is substantially similarto the through wire interconnect 14-14 (FIG. 2N). However, the throughwire interconnect 14-15 also includes a projection 37-15, such as ametal pin, a ball bump or a stud bump, on the tip portion of the wire30-15. In this embodiment, the projection 37-15 functions as a firstcontact for the through wire interconnect 14-15.

Referring to FIG. 3A, a stacked system 54 includes two semiconductorcomponents 10 stacked in a circuit side 17 to back side 18configuration. In addition, the ball contact 46 on the uppersemiconductor component 10 is bonded to the bonding member 32 on thelower semiconductor component 10 using a suitable bonding process suchas a gold to gold diffusion bond, a reflow bond, or a conductive polymerbond, such as an anisotropic conductive film (ACF) to be hereinafterdescribed. In the stacked system 54, the polymer layer 16 on the lowersemiconductor component 10 provides a planar surface for stacking. Inaddition, either the ball contacts 46 on the lower semiconductorcomponent 10, or the bonding members 32 on the upper semiconductorcomponent 10, can be configured as terminal contacts for the stackedsystem 54. Alternately, separate terminal contacts, such as solderballs, can be formed on the semiconductor components 10 in electricalcommunication with the ball contacts 46 or the bonding members 32.Previously incorporated application Ser. No. 11/296,057 disclosesmethods for forming terminal contacts.

Referring to FIG. 3B, a stacked system 56 includes two semiconductorcomponents 10 stacked in a circuit side 17 to circuit side 17configuration. In addition, the bonding members 32 on the components 10are bonded to one another using a suitable bonding process such as agold to gold diffusion bond, a reflow bond, or a conductive polymer bondsuch as an anisotropic conductive film (ACF) to be hereinafterdescribed. In the stacked system 56, the polymer layers 16 on bothcomponents 10 provide planar surfaces for stacking. In addition, theball contacts 46 can be configured as terminal contacts for the stackedsystem 56. Alternately, separate terminal contacts such as solder ballscan be formed on the semiconductor components 10 in electricalcommunication with the ball contacts 46. Previously incorporatedapplication Ser. No. 11/296,057 discloses additional semiconductorcomponents and stacked systems that can be fabricated usingsemiconductor components with through wire interconnects.

Referring to FIGS. 4A-4E, an alternate embodiment semiconductorcomponent 10A is illustrated. The semiconductor component 10A includes asubstrate 12A having a plurality of substrate contacts 20A and throughwire interconnects 14A. Each through wire interconnect 14A includes avia 28A, a wire 30A having a loop portion 50A, and a bonding member 32Abonding the wire 30A to the substrate contact 20A, substantially aspreviously described for through wire interconnects 14 (FIG. 1A). Inthis embodiment the wire 30A and the contact ball 46A (second contact)on the wire 30A are free to move in the z direction as indicated byarrow 62A (FIG. 4C).

The through wire interconnects 14A (FIG. 4C) also include polymermembers 58A (FIG. 4C) on the substrate contacts 20A (FIG. 4C), whichsupport the loop portions 50A (FIG. 4C) of the wires 30A (FIG. 4C). Thepolymer members 58A (FIG. 4C) can have a compliant, resilient orcompressible configuration. In addition, the loop portions 50A (FIG. 4C)of the wires 30A (FIG. 4C) can be embedded in the polymer members 58A(FIG. 4C) or supported by grooves or other features on the polymermembers 58A (FIG. 4C). Alternately, the polymer members 58A (FIG. 4C)can have a relatively rigid configuration with the wires 30A (FIG. 4C)supported by the surfaces thereof. In either case, the polymer members58A (FIG. 4C) protect, and maintain the planarity and the shapes of theloop portions 50A (FIG. 4C) of the wires 30A (FIG. 4C). The polymermembers 58A (FIG. 4C) also allow the tips of the loop portions 50A (FIG.4C) to be used as contacts for the through wire interconnects 14A (i.e.,first contacts as previously described, or in some cases third contactsin combination with the first contacts and the second contacts). In thiscase, the loop portions 50A (FIG. 4C) can have a first height H1 (FIG.4C) on the substrate 12A, which is greater than a second height H2 (FIG.4C) of the bonding members 32A (FIG. 4C) on the substrate 12A.

The polymer members 58A (FIG. 4C) can also be configured to provide aspring force which allows the contact balls 46A (FIG. 4C) to flex in thez-direction during electrical engagement of a test contact 64 (FIG. 6A)on a device under test 66 (FIG. 6A). The device under test 66 (FIG. 6A)can comprise a semiconductor die or wafer, or an array of semiconductordice on a semiconductor wafer or portion thereof. The polymer member 58A(FIG. 4C) also allow the tips of the loop portions 50A (FIG. 4C) of thewires 30A (FIG. 4C) to flex during electrical engagement of matingcontacts. The sidewalls of the vias 28A (FIG. 4C) can also be coveredwith a low friction insulating layer 34A (FIG. 4C), such as parylene,which allows the wires 30A to move freely within the vias 28A (FIG. 4C)during electrical engagement. The wires 30A can also include polymerlayers such as the previously described insulated bonding wire fromMicro Bond of Canada. In this case the polymer layers on the wires 30A(FIG. 4C) can help lower friction between the wires 30A (FIG. 4C), andthe vias 28A (FIG. 4C). In addition, the wires 30A (FIG. 4C) can be longenough to space the contact balls 46A (FIG. 4C) from the substrate 12A(FIG. 4C) to allow movement during electrical engagement.

The polymer members 58A (FIG. 4C) can comprise a polymer material suchas silicone, polyimide, epoxy or mold compound having a selected size,shape and durometer. In addition, the polymer members 58A (FIG. 4C) canbe formed with required sizes and shapes using a molding process, adeposition process, or a screen printing process. In the illustrativeembodiment, each through wire interconnect 14A (FIG. 4C) has anassociated polymer member 58A (FIG. 4C). However, a polymer member canbe formed to support several through wire interconnects 14A, such as allof the through wire interconnects 14A on a row of substrate contacts 20A(FIG. 4C). Also in the illustrative embodiment, the polymer members 58A(FIG. 4A) are tapered to conform to the natural shape of the wire loops50A (FIG. 4C). However, the polymer members 58A (FIG. 4A) can have anydesired shape. The polymer members 58A (FIG. 4A) can also have anydesired footprint such as a circular or polygonal, and any desiredheight. In addition, the polymer members 58A can include grooves,ridges, indentations or other features, which support the loop portions50A of the wires 30A. As another alternative the polymer members 58A canat least partially encapsulate or surround the wire loops 50A (FIG. 4C)

As shown in FIGS. 4D and 4E, the contact balls 46A, and the tips of theloop portions 50A as well, can include wear resistant outer layers 60A,which coat the surfaces of the wires 30A (FIG. 4C). For example, thewires 30A (FIG. 4C) can comprise gold, and the outer layers 60A (FIGS.4D and 4E) can comprise nickel, tungsten or a conductive polymer havingmetal particles therein. In addition to providing wear resistantsurfaces, the outer layers 60A can also enhance oxide and contaminantpenetration for making low resistance, temporary or permanent electricalconnections.

Referring to FIG. 5, an alternate embodiment 2× semiconductor component10B includes through wire interconnects 14B constructed substantially aspreviously described for the semiconductor component 10A (FIG. 4C). Assuch, the semiconductor component 10B includes polymer members 58B whichsupport loop portions 50B of the through wire interconnects 14B. Thesemiconductor component 10B also includes a first polymer layer 16B-1,which encapsulates the circuit side 17B of the semiconductor substrate12B and substantially encapsulates the loop portions 50B of the throughwire interconnects 14B. The first polymer layer 16B-1 also fills the via28B and secures the wire 30B in the vias 28B, substantially aspreviously described with the polymer material 36 (FIG. 1C). However,surfaces of the loop portions 50B of the through wire interconnects 14Bremain exposed, and function as contacts (first contacts) for thethrough wire interconnects 14B proximate to the circuit side 17B. Aswith the previous embodiment, these contacts can be coated with a wearresistant or oxide penetrating material such as nickel, or a conductivepolymer having metal particles. The semiconductor component 10B alsoincludes a second polymer layer 16B-2, which encapsulates the back side18B of the semiconductor substrate 12B, and substantially encapsulatesthe ball contacts 46B of the through wire interconnects 14B. However,surfaces of the ball contacts 46B can remain exposed, to function ascontacts (second contacts) for the through wire interconnects 14Bproximate to the back side 18B.

Referring to FIGS. 6A and 6B, a test system 68 incorporating thesemiconductor component 10A is illustrated. In the test system 68, thesemiconductor component 10A functions as an interconnect component formaking temporary electrical connections with a device under test 66. Forexample, the device under test 66 can comprise a semiconductor wafer, inwhich case the semiconductor component 10A would perform the samefunction as a probe card. Alternately, the device under test 66 cancomprise a singulated semiconductor die or semiconductor package. Inthis case the semiconductor component 10A can be contained in a testfixture, substantially as described in U.S. Pat. No. 5,519,332 entitled“Carrier For Testing An Unpackaged Semiconductor Die”, which isincorporated herein by reference.

As shown in FIG. 6A, the device under test 66 includes a plurality oftest contacts 64 that are initially aligned with the ball contacts 46Aof the through wire interconnects 14A. Alignment can be accomplishedusing optical or mechanical alignment techniques that are known in theart. As also shown in FIG. 6A, the through wire interconnects 14A areplaced in electrical communication with test circuitry 70, which isconfigured to apply test signals to the device under test 66. Previouslyincorporated application Ser. No. 11/296,057 discloses various methodsand structures for placing the through wire interconnects 14A intoelectrical communication with the test circuitry 70.

As shown in FIG. 6B, following alignment, either the semiconductorcomponent 10A, or the device under test 66, (or both) can be moved inthe z-direction to place the ball contacts 46A of the through wireinterconnects 14A into contact with the test contacts 64. In addition,the semiconductor component 10A and the device under test 66 can be heldtogether using a biasing force generated by a test fixture, a waferprober or other testing device known in the art. This establishestemporary electrical communication between the ball contacts 46A of thethrough wire interconnects 14A and the test contacts 64. As the wire 30Ais free to move in the z-direction during electrical engagement,variations in the planarity and location of the test contacts 64 can beaccommodated by movement of the ball contacts 46A. In addition, thepolymer members 58A provide spring forces for biasing the ball contacts46A against the test contacts 64 and for returning the ball contacts 46Ato their original locations following the test process. This allows theball contacts 46A to be used to align with and test another device undertest 66. Further, the outer layers 60A (FIG. 4D) on the ball contacts46A penetrate oxide layers on the test contacts 64 to provide lowresistance temporary electrical connections.

Referring to FIG. 7, an alternate embodiment test system 72incorporating the semiconductor component 10A is illustrated. In thetest system 72, the semiconductor component 10A functions as aninterconnect component for making temporary electrical connections witha device under test 66 substantially as previously described for thetest system 68 (FIG. 6A). However, in the test system 72 the loopportions 50A of the wires 30A, rather than the ball contacts 46A, makethe temporary electrical connections with the test contact 64 on thedevice under test 66. In addition, the polymer members 58A providespring forces for maintaining the location and planarity of the loopportions 50A. The polymer members 58A also provide spring forces forbiasing the loop portions 50A into the test contact 64 under a biasingforce generated by a test fixture, a wafer prober or other testingdevice known in the art. Essentially the same test system 72 (FIG. 7)can be constructed using the semiconductor component 10B (FIG. 5) inplace of the semiconductor component 10A (FIG. 7). In this case, thepolymer layer 16B-1 (FIG. 5) can be relatively compressible to allowmovement of the loop portions 50A during electrical engagement.

Referring to FIG. 8, an alternate embodiment module system 74incorporating two semiconductor components 10U, 10L having through wireinterconnects 14B is illustrated. The semiconductor components 10U, 10Lare substantially similar to the semiconductor component 10B of FIG. 5.Although only two semiconductor components 10U, 10L are illustrated, itis to be understood that the module system 74 can include any number ofstacked semiconductor components (e.g., two to twenty). The claims tofollow thus refer to at least two stacked semiconductor components. Inaddition, the semiconductor components 10U, 10L are attached andinterconnected using an anisotropic conductive film 41 which covers theback side of the lower semiconductor component 10L, and the circuit sideof the upper semiconductor component 10U. However, the semiconductorcomponents 10U, 10L can be attached and interconnected using an adhesivebond and a conductive bond between mating elements.

The module system 74 (FIG. 8) includes a module substrate 78, such as acircuit board, having a plurality of electrodes 80, which connect toother electrical elements and circuits on the module substrate 78. Inaddition, the loop portions 50B of the through wire interconnects 14B onthe lower semiconductor component 10L are bonded to the electrodes 80 onthe support substrate 78 using a bonded connection as previouslydescribed. The loop portions 50B of the through wire interconnects 14B.on the lower semiconductor component 10L can be bonded to theelectrodes 80 on the module substrate 78 using bonded connections suchas solder fillets, conductive adhesive layers, reflow bonds, ordiffusion bonds. As previously described, the loop portions 50B aresupported by the polymer members 58B, which maintain their locations andplanarity. As shown in FIG. 8, the polymer layer 16B on the lowersemiconductor component 10L also spaces and electrically insulates thelower semiconductor component 10L from the module substrate 78.Alternately, these electrical connections can be made using ananisotropic conductive film 41B placed between the polymer layer 16B onthe lower semiconductor component 10L and the substrate 78.

As shown in FIG. 8, the module system 74 also includes the anisotropicconductive film 41 which electrically connects the loop portions 50B ofthe through wire interconnects 14B on the upper semiconductor component10U with the through wire interconnects 14B on the lower semiconductorcomponent 10L. In the illustrative embodiment, the ball contacts 46B ofthe through wire interconnects 14B on the lower semiconductor component10L have been eliminated, such that electrical contact is through theanisotropic conductive film 41 to the ends of the wires 30B of thethrough wire interconnects 14B on the lower semiconductor component 10L.The anisotropic conductive film 41 and the anisotropic conductive film41B can comprise a thermally and electrically conductive Z-axis filmadhesive. On suitable Z-axis film adhesive is manufactured by Btechcorpof Brentwood, Tenn. under the product description IOB-3.

As also shown in FIG. 8, the polymer layer 16B on the uppersemiconductor component 10U contacts the anisotropic conductive film 41.Further, the polymer members 58B on the upper semiconductor component10U support the loop portions 50B and their points of contact with theanisotropic conductive film 41. In addition, the ball contacts 46B ofthe through wire interconnects 14B on the upper semiconductor component10U provide terminal contacts from the outside to the module system 74.Further, the polymer layer 16B-2 on the back side of the uppersemiconductor component 10U provides electrical insulation for the uppersemiconductor component 10U.

Referring to FIGS. 9A-9B, a wafer system 76 includes a semiconductorwafer 82 and multiple singulated semiconductor components 10 (FIGS.1A-C) bonded to the semiconductor wafer 82. Alternately, in place of thesemiconductor components 10, the wafer system 76 can include any otherpreviously described alternate embodiment semiconductor component. Thesemiconductor wafer 82 includes a plurality of semiconductor dice 84with a desired electrical configuration having die contacts 86 (FIG. 9B)in electrical communication with the integrated circuits contained onthe semiconductor dice 84. For illustrative purposes the semiconductordice 84 are illustrated as having peripheral outlines (footprints) thatare about the same size but slightly larger than the peripheral outlines(footprints) of the semiconductor components 10.

As shown in FIG. 9B, the bonding members 32 of the through wireinterconnects 14 on the semiconductor components 10 are bonded to thedie contacts 86 on the semiconductor dice 84 contained on thesemiconductor wafer 82. In addition, the polymer layers 16 on thesemiconductor components 10 provide planar surfaces, which electricallyinsulate the components 10 from the semiconductor dice 84. In addition,adhesive layers 88 can be used to attach the semiconductor components 10to the semiconductor wafer 82. If desired the adhesive layers 88 cancomprise a conductive adhesive, such as the previously described Z-axisfilm adhesives to provide electrical conductivity as well as mechanicalattachment. Further, the ball contacts 46 on the semiconductorcomponents 10 provide outside electrical connection points (secondcontacts) to the semiconductor components 10 and the correspondingsemiconductor dice 84 on the semiconductor wafer 82. Alternately, thesemiconductor components 10 can be flipped and the ball contacts 46bonded to the die contacts 86 on the semiconductor dice 84. In thiscase, the bonding members 32 would be on outside, and could provideoutside electrical connection points (second contacts). As anotheralternative, the loop portions 50A (FIG. 4B) or 50B (FIG. 5) ofsemiconductor components 10A (FIG. 4B) or 10B (FIG. 5) could be bondedto the die contacts 86 (FIG. 9B) substantially as shown in FIG. 8.

Referring to FIG. 10, a wafer to wafer system 90 is substantiallysimilar to the wafer system 76 (FIGS. 9A-9B) but the semiconductorcomponents 10 are contained on a second semiconductor wafer 92.Alternately, in place of the semiconductor components 10, the wafer towafer system 90 can include any of the previously described alternateembodiment semiconductor components contained on the secondsemiconductor wafer 92.

Referring to FIGS. 11A-11D and 12A-12C, a method for fabricating thesemiconductor component 10 (FIG. 1A) is illustrated. Essentially thesame method can be used to fabricate any of the previously describedalternate embodiments of the semiconductor component 10. In theillustrative embodiment, the method comprises a wafer level fabricationmethod. However, it is to be understood that the method can also beperformed on singulated components with a die level fabrication method.

Initially, as shown in FIGS. 11A and 12A, a component substrate 94containing a plurality of the semiconductor substrates 12 is provided.The component substrate 94 can comprise a semiconductor wafer or aportion of a wafer containing semiconductor dice. Alternately thecomponent substrate 94 can comprise a panel containing semiconductorpackages, such as molded array packages. In addition, the componentsubstrate 94 can have a desired thickness, such as the previouslydescribed thickness T (FIG. 1C) for the semiconductor substrates 12.

As shown in FIG. 11A, a plurality of through wire interconnects 14 areformed on the semiconductor substrates 12 contained on the componentsubstrate 94. Previously incorporated U.S. application Ser. Nos.11/102,408 and 11/296,057 describe methods and systems for fabricatingthe through wire interconnects 14. Each through wire interconnect 14includes the via 28 through the substrate contact 20 and thesemiconductor substrate 12, the wire 30 in the via 28 bonded to thesubstrate contact 20, and the ball contact 46 (second contact) on thewire 30. Each through wire interconnect 14 also includes the bondingmember 32 (second contact) on the substrate contact 20 and the wire 30having the tip portion 48 forming a first contact substantially aspreviously described. Alternately, in place of the through wireinterconnects 14, any of the previously described alternate embodimentof through wire interconnects can be fabricated on the semiconductorsubstrates 12 contained on the component substrate 94.

Each through wire interconnect 14 can also include the polymer material36 (FIG. 11A) in the via 28 substantially as previously described. Thepolymer material 36 can be deposited into the via 28 and around the wire30 in viscous form and then cured to harden. In addition, excess polymermaterial, such as material on the circuit side 17 of the semiconductorsubstrate 12 could then be removed using a spacer etch process with asuitable etchant. Alternately, the polymer material 36 can be depositedinto the via 28 in viscous form prior to placement of the wire 30. Inthis case, the wire 30 would be pushed into the viscous polymer material36, which would then be cured to harden around the wire 30. This wouldeliminate the need for a spacer etch to remove excess material. Inaddition, the via could initially be a non vented counterbore to preventthe egress of liquids or slurries during a subsequent back side thinningstep, as described in previously incorporated U.S. application Ser. Nos.11/102,408 and 11/296,057. The polymer material 36 (FIG. 11A) can bedeposited using a suitable deposition process such as screen printing,stenciling or deposition using a nozzle or a material dispensing system.

The polymer material 36 (FIG. 11A) can comprise an electricallyinsulating curable polymer, such as a polyimide, epoxy, a silicone or amold compound. Also, the polymer material 36 can include fillers, suchas silicates, configured to reduce the coefficient of thermal expansion(CTE) and adjust the viscosity of the dielectric material. Suitablecurable polymers are manufactured by Shinitsu of Japan, and DexterElectronic Materials of Rocky Hill, Conn. Following curing, the polymermaterial 36 provides a potting structure which secures and electricallyinsulates the wire 30 in the via 28. Alternately, for some applications,the polymer material 36 in the via 28 can comprise an electricallyconductive material.

Next, as shown in FIG. 11B, a film assisted molding system 96 isprovided. Suitable film assisted molding systems are available fromBoschman Technologies b.v. Nieuwgraaf, The Netherlands, and by Yamada ofJapan. The film assisted molding system 96 allows ultra thinsemiconductor components to be encapsulated on one or more surfaces. Thefilm assisted molding system 96 includes a first mold 98 for supportingthe circuit sides 17 of the semiconductor substrates 12 on the componentsubstrate 94, and a second mold 100 for supporting the back sides 18 ofthe semiconductor substrates 12 on the component substrate 94. The firstmold 98 includes a plurality of mold cavities 102 configured to mold thepolymer layer 16 (FIG. 1B) on the semiconductor substrates 12. In theillustrative embodiment, the components 10 (FIG. 11D) are moldedseparately, which is referred to as a matrix substrate configuration.Alternately, multiple components can be molded together, which isreferred to as an array substrate configuration.

As shown in FIGS. 11B and 12B, the first mold 98 includes a mold film104 which follows the contour of the mold cavities 102. The first mold98, the mold film 104 and the mold cavities 102 are sized and shapedsuch that the tip portions 48 of the bonding members 32 become embeddedin the mold film 104 and protected from the subsequent molding step.These elements are also configured to form the polymer layers 16 (FIG.11D) with a selected thickness. A representative range for the selectedthickness can be from 10 μm to 500 μm.

Next, as shown in FIG. 11C, a molding step is performed in which aplastic molding material, such as a thermoset polymer, is injected intothe mold cavities 102 to form the polymer layers 16 on the circuit sides17 of the semiconductor substrates 12. However, during the molding step,the tip portions 48 of the bonding members 32 are protected by the moldfilm 104 from the plastic molding material.

As shown in FIGS. 11D and 12C, the polymer layers 16 encapsulate thecircuit sides 17 of the semiconductor substrates 12. The polymer layers16 can be made with planar surfaces and precise thicknesses. Similarly,the tip portions 48 of the bonding members 32 can project from thepolymer layers 16 by a selected distance. A representative range forthis selected distance can be from 10 μm to 75 μm. As only one side ofeach semiconductor substrate 12 is encapsulated, the semiconductorcomponents 10 are referred to as having a 1× configuration. However,essentially the same molding process can be used to form a 2× or a 6×component. For example, essentially the same molding process can be usedto encapsulate the edges and back sides 18 of the semiconductorsubstrates 12, while leaving tip portions of the ball contacts 46 (FIG.11D) exposed. As will be further explained, essentially the same moldingprocess can also be used to form both the polymer layers 16 forencapsulation, and the polymer material 36 (FIG. 1C) in the vias 28(FIG. 1C).

Essentially the same molding process can also be used to have selectedareas on the component substrate 94, or on the individual semiconductorsubstrates 12, unencapsulated by the polymer layers 16. For example, thepixel array of an imager component can remain unencapsulated. In thiscase, the molding film 104 can be configured to cover or “gasket off”the pixel arrays, or other selected areas of the semiconductorsubstrates 12, from being encapsulated by the mold compound. As anotheralternative, “blocks” or “pedestals” of a compressible polymer, such assilicone, can be placed in a selected pattern on the molding film 104,or on the component substrate 94. During the molding step, the “blocks”or “pedestals” would be compressed between the component substrate 94and the molding film 104. Where the “blocks” or “pedestals” are inintimate contact with an area or an element (e.g., loop portions50A-FIG. 4B) on the component substrate 94, the area or element would befree of the plastic molding material. The “blocks” or “pedestals” couldthen be removed after the molding step. Alternately, the “blocks” or“pedestals” could be left attached to the component substrate 94, andused to attach lenses over the pixel arrays of imager components.

Following the molding step, a singulating step, such as sawing,scribing, liquid jetting, or laser cutting through a liquid, can beperformed to singulate the semiconductor components 10 from thecomponent substrate 94 with desired footprints, such as chip scaleoutlines. Alternately, a wafer sized component can be provided whichcontains multiple unsingulated semiconductor substrates 12.

Referring to FIGS. 13A-13B, a method for fabricating the semiconductorcomponent 10A (FIG. 4B) with through wire interconnects 14A (FIG. 4B)having polymer members 58A (FIG. 4B) is illustrated. Initially, as shownin FIG. 13A, the via 28A and the insulating layer 34A are formed in thesubstrate contact 20A substantially as described in previouslyincorporated U.S. application Ser. Nos. 11/102,408 and 11/296,057. Asalso described in these applications, the via 28A is initially acounterbore or blind hole having a vent opening 108. Following a wirebonding step, the back side 18A of the substrate is thinned to exposethe ball contact 46A (FIG. 13B).

As also shown in FIG. 13A, the polymer members 58A can be formed on thesubstrate contacts 20A. The polymer members 58A can comprise a polymermaterial such as silicone, polyimide, epoxy or mold compound. Inaddition, the polymer members 58A can have a desired size, shape anddurometer. Further, the polymer members 58A can be fabricated using asuitable process, such as depositing, molding or screen printing aviscous or semi viscous (B-stage) curable polymer onto the substratecontacts 20A, and if desired other portions of the circuit side 17A ofthe semiconductor substrate 12A. The polymer members 58A can also beformed by placing pre-formed adhesive polymer elements on the substratecontacts 28A.

Next, as shown in FIG. 13B, a wire bonder having a bonding capillary 110can be provided. Preferably the wire bonder is configured to perform anultra fine pitch (e.g., <65 μm) wire bonding process. Suitable wirebonders are manufactured by Kulicke & Soffa Industries Inc. of WillowGrove, Pa., and Palomar of Carlsbad, Calif. One suitable wire bonder isan “AT PREMIER” large area ball bonder manufactured by Kulicke & SoffaIndustries Inc., having a total bond placement accuracy of about ±5 μmat pitches down to about 65 μm. Bonding capillaries are available fromSPT (Small Precision Tools) of Petaluma, Calif., and from Kulicke &Soffa Industries Inc.

The bonding capillary 110 (FIG. 13B) is configured to form a continuouslength of bonding wire into the wire 30A (FIG. 13B) for the through wireinterconnect 14A (FIG. 13B), and to form the bonded connections 42A withthe substrate contacts 20A. Previously incorporated U.S. applicationSer. Nos. 11/102,408 and 11/296,057 further describe the bonding step.However, in this embodiment the bonding capillary 110 is controlled suchthat the wires 30A follow the contour of the polymer members 58A, andhave the high loop portions 50A. Further, the polymer members 58A can bein a semi-cured or B-stage condition during the bonding step, such thatthe loop portions 50A of the wires 30A are in effect embedded in thepolymer members 58A. Further, the outside surfaces of the loop portions50A can have outer layers 60A (FIG. 4D) formed of a wear resistant metalsuch as nickel. The wear resistant metal can be provided on the wires30A from the outset, or can be plated on the loop portions 50A followingthe bonding step.

Following the bonding step, the bonding members 32A (FIG. 4B) can beformed on the bonded connections 42A, using a suitable process such asball bumping, stud bumping or reflow bonding, as further described inpreviously incorporated U.S. application Ser. Nos. 11/102,408 and11/296,057. The semiconductor substrate 12A can then be thinned from theback side to expose the ball contacts 46A. However, prior to thethinning step the film assisted molding process shown in FIGS. 11A-11Dand 12A-12C can be used to form polymer layers (e.g., 16B-1 in FIG. 5)as required.

Referring to FIG. 14, essentially the same film assisted molding processshown in FIGS. 11A-11D and 12A-12C, can be used to fabricate analternate embodiment encapsulated semiconductor component 10E. Theencapsulated semiconductor component 10E includes a polymer layer 16Ewhich encapsulates the circuit side 17, the back side 18, and the sides52 of the semiconductor substrate 12. In this embodiment, the polymerlayer 16E encapsulates all six sides of the semiconductor substrate 12,and the component 10E is referred to as 6× component. Alternately, apolymer layer can be configured to encapsulate only the circuit side 17and the back side 18 of the substrate 12, such that a 2× component wouldbe provided. U.S. Pat. No. 6,908,784, which is incorporated herein byreference, discloses different configurations of encapsulatedsemiconductor components.

Referring to FIG. 15A-15D, essentially the same film assisted moldingprocess shown in FIGS. 11A-11D and 12A-12C, can be used to fabricate anyof the previously described through wire interconnects in which thepolymer layer which encapsulates the component, also fills the via inplace of the polymer material. For illustrative purposes fabrication ofthe semiconductor component 14-11 of FIG. 2K is illustrated.

Initially, as shown in FIG. 15A, the via 28-11 and the insulating layer34-11 are formed in the substrate contact 20-11 substantially aspreviously described for FIG. 13A. In addition, a vent 108-11 to the via28-11 is formed. Next as shown in FIG. 15B, the bonding member 32-11 isformed on the substrate contact 20-11. The bonding member 32-11 cancomprise a stud bump, or a ball bump, bonded to the substrate contact20-11 using a wire bonder, a stud bumper, or a ball bumper. Alternately,the bonding member 32-11 can comprise a solder bump, a weldedconnection, or a conductive polymer connection.

Next, as shown in FIG. 15C, a bonding capillary 112 is used to place thewire 30-11 in the via 28-11, and to form the bonded connection 42-11between the wire 30-11 and the bonding member 32-11. The wire 30-11 cantouch the via 28-11 as shown or can be suspended in the via 28-11.

Next, as shown in FIG. 15D, a film assisted molding process is performedsubstantially as shown in FIGS. 11A-11D and 12A-12C to form the polymerlayer 16-11. During the molding process, the mold film 104 protectsportions of the wire 30-11 and the bonding member 32-11, so that theyremain unencapsulated as previously described. In addition, the moldcompound flows into the via 28-11 to fill the via 28-11 and secure thewire 30-11. Although the wire 30-11 may be pushed during molding, andsome buckling can occur, this can be tolerated as long as shorting toother elements by the wire 30-11, and removal of the insulating layer34-11 does not occur. During the molding process, the vent 108-11 allowsair to escape from the via 28-11 and the molding compound to flow freelyinto the via 28-11. A vacuum can also be applied to the vent 108-11 tofacilitate filling of the via 28-11 by the mold compound. During themolding process, the vent 108-11 can also function to center the wire30-11 in the via 28-11. In addition, the molding process can beperformed to prevent the molding compound from flowing through the vent108-11 onto the back side of the substrate 12-11. However, for someapplications the vent 108-11 may not be required, such as when a vacuumis pulled on the mold cavities 102 (FIG. 11B). Following the moldingprocess, the mold film 104 can be removed, and the back side of thesubstrate 12-11 thinned by etching or grinding to expose the ballcontact 46-11.

Referring to FIGS. 16A-16C, a method for fabricating a semiconductorcomponent 10-13 (FIG. 16C) is illustrated using a film frame moldingprocess to form the polymer layer 16-13 (FIG. 16C) for the semiconductorcomponent 10-13 (FIG. 16C). Initially, as shown in FIG. 16A, a pluralityof semiconductor substrates 12-13 are provided on a component substrate94, such as a semiconductor wafer, substantially as previously describedand shown in FIG. 12A. In addition, through wire interconnects 14-13 areformed on the semiconductor substrates 12-13, substantially aspreviously described and shown in FIG. 12A. The through wireinterconnects 14-13 also include conductors 31-13 and pads 33-13,substantially as previously described and shown in FIG. 2M.

As shown in FIG. 16B, following fabrication of the through wireinterconnects 14-13, the component substrate 94 is singulated intoseparate semiconductor substrates 12-13. The singulation step can beperformed using a suitable process such as saw cutting, etching orliquid jetting. In addition, following singulation, the semiconductorsubstrates 12-13 can be tested by placing the pads 33-13 in electricalcommunication with testing circuitry 114. For example, the semiconductorsubstrates 12-13 can be placed in a test fixture, substantially asdescribed in U.S. Pat. No. 5,519,332 entitled “Carrier For Testing AnUnpackaged Semiconductor Die”, which is incorporated herein byreference. Each semiconductor substrate 12-13 can thus be certified as aknown good die (KGD). Alternately, the testing can be performed at thewafer level on the semiconductor substrates 12-13 while they are stillcontained on the component substrate 94. In this case, the pads 33-13provide electrical connection points for a probe card or other waferlevel test device.

As also shown in FIG. 16B, the singulated and tested semiconductorsubstrates 12-13 can be placed on a film frame 116. The film frame 116can comprise a conventional film frame used in the semiconductorindustry. In addition, a conventional pick and place process can be usedto place the semiconductor substrates 12-13 on the film frame 116.

Next, as shown in FIG. 16C, a film assisted molding process,substantially as previously described and shown in FIGS. 11A-11D, can beperformed to form the polymer layer 16-13 for the semiconductorcomponent 10-13. However, in this case the semiconductor substrates12-13 are contained on the film frame 116 during the film assistedmolding process. As previously described, the tip portions of thebonding members 32-13 of the through wire interconnects 14-13 areprotected by a mold film 104 (FIG. 11B) and remain unencapsulated duringthe film assisted molding process. As also shown in FIG. 16C, followingthe film assisted molding process the semiconductor components 10-13 aresingulated by cutting through the polymer material between adjacentsemiconductor substrates 12-13 on the film frame 116. In FIG. 16C, thesaw cuts are indicated by cut lines 118. With this process the polymerlayer 16-13 covers the circuit side and four edges of the semiconductorsubstrates 12-13, such that the completed semiconductor components 10-13have a 5× configuration.

In an illustrative embodiment a semiconductor component includes asemiconductor substrate having a first side (circuit side), a secondside (back side), and a plurality of integrated circuits. Thesemiconductor component also includes a plurality of substrate contactson the first side, a plurality of through wire interconnects (TWI)bonded to the substrate contacts, and a polymer layer on the first sideencapsulating at least portions of the through wire interconnects.

Each through wire interconnect (TWI) includes a via through a substratecontact and through the substrate to the second side, a wire in the viabonded to the substrate contact, a first contact on the wire proximateto the first side, and a second contact on the wire proximate to thesecond side. In the illustrative embodiment the first contact comprisesa tip portion of the bonding member on the substrate contactencapsulated by the polymer layer, and the second contact comprises anexposed end of the wire.

The semiconductor component can also include a polymer member on thesubstrate contact which supports and maintains a planarity of a loopportion of the wire. In addition, the loop portion of the wire can beconfigured as a third contact with the polymer member providing a forcefor making a connection with a mating contact on a device under test ora next level substrate. The contacts on the wire can also include outerlayers configured to provide abrasion resistance, and enhancedpenetration of oxide or contaminants on the mating contact.

The semiconductor component can be used as a stand alone device, or incombination with other semiconductor components to fabricatesemiconductor systems. The semiconductor systems can include singulatedcomponents bonded to one another (singulated system), or singulatedsemiconductor components bonded to a semiconductor wafer (wafer system),or semiconductor components contained on a semiconductor wafer bonded toanother semiconductor wafer (wafer to wafer system). With each system,the through wire interconnects (TWI) provide a signal transmissionsystem, and bonding structures between adjacent stacked components andnext level substrates as well. The semiconductor component can also beused to fabricate test systems with the through wire interconnects (TWI)functioning as contact structures for making temporary and/or permanentelectrical connections with a device under test.

The method for fabricating a semiconductor component with through wireinterconnects (TWI) includes the steps of: providing a semiconductorsubstrate with substrate contacts, forming vias through the substrate,placing the wires in the vias, bonding the wires to the substratecontacts, forming bonding members on the wires and the substratecontacts, and forming a polymer layer on the first side substantiallyencapsulating loop portions of the wires and the bonding members. Thepolymer layer can be formed using a film assisted molding processincluding the steps of: forming a mold film on tip portions of thebonding members, molding the polymer layer, and then removing the moldfilm to expose the tip portions of the bonding members.

While a number of exemplary aspects and embodiments have been discussedabove, those of skill in the art will recognize certain modifications,permutations, additions and subcombinations thereof. It is thereforeintended that the following appended claims and claims hereafterintroduced are interpreted to include all such modifications,permutations, additions and sub-combinations as are within their truespirit and scope.

1. A semiconductor component comprising: a substrate having a firstside, a substrate contact on the first side, a second side, and a viaextending through the substrate from the first side to the second side;a wire in the via attached to the substrate contact; a first contact onthe wire proximate to the first side; a second contact on the wireproximate to the second side; and a polymer layer on the first side atleast partially encapsulating the wire while leaving the first contactexposed.
 2. The semiconductor component of claim 1 wherein the viaextends through the substrate contact, and the wire is looped out of thevia and bonded to the substrate contact.
 3. The semiconductor componentof claim 1 further comprising a bonding member on the substrate contactattached to the wire, and wherein the first contact comprises a tipportion of the bonding member unencapsulated by the polymer layer. 4.The semiconductor component of claim 1 wherein the first contactcomprise a loop portion of the wire unencapsulated by the polymer layer.5. The semiconductor component of claim 1 wherein the second contactcomprises an end of the wire.
 6. The semiconductor component of claim 1wherein the second contact comprises a bump, a pad, a ball, a projectionor a surface on the wire.
 7. The semiconductor component of claim 1wherein the substrate comprises a semiconductor substrate having atleast one integrated circuit in electrical communication with thesubstrate contact.
 8. The semiconductor component of claim 1 furthercomprising a polymer member on the substrate contact supporting a loopportion of the wire.
 9. The semiconductor component of claim 1 furthercomprising at least one second substrate on the substrate having asecond through wire interconnect in electrical communication with thethrough wire interconnect.
 10. The semiconductor component of claim 1further comprising a conductive polymer layer on the substrateelectrically connecting the through wire interconnect to a secondsubstrate.
 11. The semiconductor component of claim 1 further comprisingan insulating layer in the via or on the wire.
 12. The semiconductorcomponent of claim 1 further comprising a polymer material in the viasurrounding the wire.
 13. The semiconductor component of claim 1 whereinthe polymer layer extends into the via and surrounds the wire.
 14. Thesemiconductor component of claim 1 further comprising a second polymerlayer at least partially encapsulating the second side while leaving thesecond contact exposed.
 15. The semiconductor component of claim 1further comprising a pad on the first side in electrical communicationwith the substrate contact.
 16. The semiconductor component of claim 1wherein the first contact comprises a projection on a loop portion ofthe wire.
 17. The semiconductor component of claim 1 wherein the polymerlayer substantially encapsulates the first side and peripheral edges ofthe substrate.
 18. The semiconductor component of claim 1 wherein thepolymer layer substantially encapsulates the first side and the secondside of the substrate.
 19. The semiconductor component of claim 1wherein the polymer layer substantially encapsulates the first side andthe wire in the via.
 20. The semiconductor component of claim 1 whereinthe wire includes a metal surface configured as the first contact or thesecond contact.
 21. A semiconductor component comprising: asemiconductor substrate having a first side, a substrate contact on thefirst side, and a second side; a via in the substrate contact and thesubstrate extending from the first side to the second side; a wire inthe via bonded to the substrate contact; a bonding member on the wireand the substrate contact having a portion configured as a firstcontact; and a polymer layer on the first side at least partiallyencapsulating the wire and the bonding member while leaving the firstcontact exposed.
 22. The semiconductor component of claim 21 furthercomprising a second contact on an end of the wire proximate to thesecond side.
 23. The semiconductor component of claim 22 wherein thesecond contact comprises a surface, a bump, a ball or a projection onthe wire.
 24. The semiconductor component of claim 22 further comprisinga third contact on the wire comprising a loop portion of the wireproximate to the first side.
 25. The semiconductor component of claim 22wherein the bonding member comprises a stud bump, a double bump, a ballbump, a solder bump or a conductive polymer bump.
 26. The semiconductorcomponent of claim 22 wherein the semiconductor substrate comprises athinned semiconductor die.
 27. The semiconductor component of claim 22wherein the semiconductor substrate comprises a semiconductor wafer. 28.The semiconductor component of claim 22 further comprising an insulatinglayer in the via or on the wire configured to insulate the wire from thesemiconductor substrate.
 29. The semiconductor component of claim 22further comprising a polymer material in the via at least partiallyencapsulating the wire.
 30. The semiconductor component of claim 22further comprising a polymer member on the substrate contact supportinga loop portion of the wire.
 31. The semiconductor component of claim 22further comprising a second polymer layer on the second side.
 32. Thesemiconductor component of claim 22 wherein the polymer layer extendsinto the via and secures the wire in the via.
 33. The semiconductorcomponent of claim 22 wherein the polymer layer encapsulates five sidesof the substrate.
 34. A semiconductor component comprising: asemiconductor substrate having a first side, a second side, anintegrated circuit, a substrate contact on the first side in electricalcommunication with the integrated circuit; a through wire interconnecton the semiconductor substrate comprising a via through the substratecontact and the substrate to the second side, a wire in the via having aloop portion and a bonded connection with the substrate contact, abonding member on the wire and the substrate contact having a firstcontact thereon, and a second contact on the wire in the via proximateto the second side; and a polymer layer on the first side encapsulatingthe loop portion while leaving the first contact exposed.
 35. Thesemiconductor component of claim 34 further comprising a polymermaterial surrounding the wire in the via.
 36. The semiconductorcomponent of claim 34 wherein the polymer layer extends into the via andsecures the wire in the via.
 37. The semiconductor component of claim 34further comprising at least one second semiconductor substrate on thesemiconductor substrate having a second through wire interconnect bondedto the through wire interconnect.
 38. The semiconductor component ofclaim 37 further comprising a conductive polymer layer bonding thesecond semiconductor substrate to the semiconductor substrate andelectrically interconnecting the second through wire interconnect to thethrough wire interconnect.
 39. The semiconductor component of claim 37wherein the semiconductor substrate comprises a thinned die.
 40. Thesemiconductor component of claim 37 wherein the semiconductor substratecomprises a semiconductor wafer.
 41. The semiconductor component ofclaim 37 wherein the first contact comprises a tip portion of thebonding member.
 42. The semiconductor component of claim 37 wherein thefirst contact comprises a stud bump and the wire is bonded to a tipportion thereof.
 43. The semiconductor component of claim 37 wherein thefirst contact comprises a double bump and the wire is bonded to a centerportion thereof.
 44. The semiconductor component of claim 37 furthercomprising a pad on the first side in electrical communication with thesubstrate contact.
 45. The semiconductor component of claim 37 whereinthe second contact comprises a surface, a bump, a ball or a projectionon the wire.
 46. A semiconductor component comprising: a semiconductorsubstrate having a first side, a substrate contact on the first side,and a second side; a via in the substrate contact and the substrateextending from the first side to the second side; a wire in the viabonded to the substrate contact having a loop portion proximate to thefirst side; a polymer member on the substrate contact supporting theloop portion; and a first contact on the wire.
 47. The semiconductorcomponent of claim 46 wherein the first contact comprises an exposedsurface of the loop portion.
 48. The semiconductor component of claim 46wherein the first contact comprises a projection or a bump on the loopportion.
 49. The semiconductor component of claim 46 wherein the firstcontact includes a layer configured to enhance wear resistance orpenetration of a mating contact on a second semiconductor component. 50.The semiconductor component of claim 46 further comprising a polymerlayer on the first side substantially encapsulating the loop portionwhile leaving the first contact exposed.
 51. The semiconductor componentof claim 46 further comprising a second contact on an end of the wireproximate to the second side.
 52. The semiconductor component of claim46 further comprising a bonding member on the substrate contact having atip portion configured as another contact.
 53. The semiconductorcomponent of claim 46 wherein the wire is free to move in the via. 54.The semiconductor component of claim 46 wherein the wire is secured tothe via by a polymer material in the via.
 55. The semiconductorcomponent of claim 46 wherein the wire is secured to the via by apolymer layer on the first side and in the via.
 56. A semiconductorcomponent comprising: a semiconductor substrate having a first side, asecond side, an integrated circuit, a substrate contact on the firstside in electrical communication with the integrated circuit; a throughwire interconnect on the semiconductor substrate comprising a viathrough the substrate contact and the substrate to the second side, awire in the via having a loop portion configured as a first contact anda bonded connection with the substrate contact, and a second contact onan end of the wire proximate to the second side; and a polymer member onthe substrate contact supporting the loop portion.
 57. The semiconductorcomponent of claim 56 further comprising a polymer layer on the firstside encapsulating the loop portion while leaving the first contactexposed.
 58. The semiconductor component of claim 57 wherein the polymerlayer encapsulates the first side and peripheral edges of the substrate.59. The semiconductor component of claim 57 wherein the polymer layerencapsulates the first side and extends into the via securing the wireto the via.
 60. The semiconductor component of claim 56 furthercomprising a second polymer layer encapsulating the second side whileleaving the second contact exposed.
 61. The semiconductor component ofclaim 56 further comprising a bonding member on the substrate contactand the bonded connection.
 62. The semiconductor component of claim 56wherein the semiconductor substrate comprises a thinned semiconductordie or wafer.
 63. A semiconductor system comprising: a first substratehaving a first side, a second side, a substrate contact on the firstside, and a via extending through the substrate contact and thesubstrate from the first side to the second side; a through wireinterconnect on the first substrate comprising a wire in the via bondedto the substrate contact, a first contact on the wire proximate to thefirst side, a second contact on the wire proximate to the second side,and a polymer layer on the first side at least partially encapsulatingthe wire while leaving the first contact exposed; and at least onesecond substrate stacked on the first substrate having a second throughwire interconnect electrically connected to the first contact or to thesecond contact.
 64. The semiconductor system of claim 63 wherein thefirst substrate and the second substrate comprise thinned semiconductordice or thinned semiconductor wafers.
 65. The semiconductor system ofclaim 63 wherein the first substrate comprises a thinned semiconductordie and the second substrate comprises a semiconductor wafer.
 66. Thesemiconductor system of claim 63 further comprising an anisotropicconductive polymer film attaching the second substrate to the firstsubstrate and electrically connecting the second through wireinterconnect to the first contact or the second contact.
 67. Thesemiconductor system of claim 63 further comprising a second anisotropicconductive polymer film attaching the first substrate to anothersubstrate and electrically connecting the first through wireinterconnect to an electrode on the substrate.
 68. A semiconductorsystem comprising: a first substrate having a first side, a second side,an integrated circuit, a substrate contact on the first side inelectrical communication with the integrated circuit; a through wireinterconnect on the first substrate comprising a via through thesubstrate contact and the substrate to the second side, a wire in thevia having a loop portion configured as a first contact and a bondedconnection with the substrate contact, a second contact on an end of thewire proximate to the second side, and a polymer member on the substratecontact supporting the loop portion; and at least one second substratestacked on the first substrate having a second through wire interconnectbonded to the first contact or to the second contact.
 69. Thesemiconductor system of claim 68 wherein the first substrate and thesecond substrate comprise thinned semiconductor dice.
 70. Thesemiconductor system of claim 68 wherein the first substrate comprises athinned semiconductor die and the second substrate comprises asemiconductor wafer.
 71. The semiconductor system of claim 68 whereinthe first substrate comprises a first semiconductor wafer and the secondsubstrate comprises a second semiconductor wafer.
 72. The semiconductorsystem of claim 68 further comprising an anisotropic conductive polymerfilm attaching the second substrate to the first substrate andelectrically connecting the second through wire interconnect to thefirst contact or the second contact.
 73. A semiconductor test systemcomprising: a device under test comprising a test contact; a substratehaving a first side, a substrate contact on the first side, and a secondside; and a through wire interconnect on the substrate comprising a viain the substrate contact and the substrate extending from the first sideto the second side, a wire in the via bonded to the substrate contacthaving a loop portion proximate to the first side, a polymer member onthe substrate contact supporting the loop portion, and a contact on anend of the wire configured to make a temporary electrical connectionwith the test contact under a biasing force applied by the polymermember.
 74. The semiconductor test system of claim 73 wherein the deviceunder test comprises a semiconductor die or an array of dice.
 75. Thesemiconductor test system of claim 73 wherein the device under testcomprises a semiconductor wafer.
 76. A method for fabricating asemiconductor component comprising: providing a substrate having a firstside, a second side and a substrate contact; forming a via in thesubstrate contact and the substrate to the second side; placing a wirein the via; forming a first contact on the wire proximate to the firstside and a second contact on the wire proximate to the second side; andforming a polymer layer on the first side leaving the first contactexposed.
 77. The method of claim 76 wherein the forming the polymerlayer step comprises a film assisted molding process in which the firstcontact is protected by a molding film during a molding step.
 78. Themethod of claim 76 further comprising forming a bonding member on thesubstrate contact attached to the wire, and wherein the first contactcomprises a tip portion of the bonding member unencapsulated by thepolymer layer.
 79. The method of claim 76 wherein the first contactcomprise a loop portion of the wire unencapsulated by the polymer layer.80. The method of claim 76 wherein the second contact comprises an endof the wire.
 81. The method of claim 76 wherein the second contactcomprises a bump, a pad, a ball or a surface on the wire.
 82. The methodof claim 76 wherein the substrate comprises a semiconductor substratehaving at least one integrated circuit in electrical communication withthe substrate contact.
 83. The method of claim 76 further comprisingforming a polymer member on the substrate contact supporting a loopportion of the wire.
 84. The method of claim 76 further comprisingattaching at least one second substrate on the substrate having a secondthrough wire interconnect in electrical communication with the throughwire interconnect.
 85. The method of claim 76 wherein the forming thepolymer layer step is performed using a film assisted molding processwith the substrate contained on a semiconductor wafer comprising aplurality of substrates.
 86. The method of claim 76 wherein the formingthe polymer layer step is performed using a film assisted moldingprocess with the substrate contained on a film frame.
 87. A method forfabricating a semiconductor component comprising: providing a substratehaving a first side, a second side and a substrate contact; forming avia in the substrate contact and the substrate to the second side;placing a wire in the via; forming a bonding member on the wire and thesubstrate contact; and forming a polymer layer on the first side leavingat least a portion of the bonding member exposed.
 88. The method ofclaim 87 wherein the bonding member a stud bump, a ball bump, a doublebump, a solder bump or a conductive polymer bump.
 89. The method ofclaim 87 wherein the forming the polymer layer step comprises a filmassisted molding process.
 90. The method of claim 87 wherein the formingthe polymer layer step comprises a film assisted molding process inwhich a mold film covers the portion of the bonding member.
 91. Themethod of claim 87 wherein the forming the polymer layer step isperformed using a film assisted molding process with the substratecontained on a semiconductor wafer comprising a plurality of substrates.92. The method of claim 87 wherein the forming the polymer layer step isperformed using a film assisted molding process with the substratecontained on a film frame.
 93. The method of claim 87 further comprisingstacking a second substrate on the substrate having a second contactelectrically connected to the bonding member.
 94. The method of claim 87further comprising stacking a second substrate on the substrate having asecond contact electrically connected to the bonding member using ananisotropic conductive adhesive.
 95. The method of claim 87 furthercomprising stacking a second substrate on the substrate having a secondbonding member electrically connected to the bonding member.
 96. Themethod of claim 87 further comprising stacking a second substrate on thesubstrate having a second wire electrically connected to the wire. 97.The method of claim 87 further comprising forming a polymer material inthe via surrounding the wire.
 98. The method of claim 87 wherein theforming the polymer layer step deposits the a polymer material in thevia surrounding the wire.
 99. A method for fabricating a semiconductorcomponent comprising: providing a semiconductor substrate having anintegrated circuit and a substrate contact in electrical communicationwith the integrated circuit; forming a via in the contact and thesubstrate; placing a wire in the via; bonding the wire to the substratecontact; forming a first contact on the first side in electricalcommunication with the wire; covering the first contact; and forming apolymer layer on the first side while the first contact remains covered.100. The method of claim 99 further comprising forming a second contacton the wire proximate to the second side.
 101. The method of claim 99wherein the covering step and the forming the polymer layer stepcomprise a film assisted molding process.
 102. The method of claim 99wherein the substrate is contained on a semiconductor wafer during theforming the polymer layer step.
 103. The method of claim 99 wherein thesubstrate is contained on a film frame during the forming the polymerlayer step.
 104. The method of claim 99 wherein the covering stepcomprises covering the first contact with a mold film and the formingthe polymer layer step comprises film assisted molding.
 105. The methodof claim 99 wherein the placing step and the bonding step are performedusing a bonding capillary.
 106. The method of claim 99 furthercomprising depositing a polymer material in the via and around the wire.107. The method of claim 99 wherein the forming the polymer layer stepdeposits polymer material in the via surrounding the wire.
 108. Themethod of claim 99 further comprising forming a bonding member on thewire and on the substrate contact having a portion configured as thefirst contact.
 109. The method of claim 99 further comprising forming asecond contact on the wire proximate to the second side.
 110. The methodof claim 99 further comprising forming a wear resistant or penetratinglayer on the second contact.
 111. The method of claim 99 furthercomprising forming a pad on the first side in electrical communicationwith the substrate contact.
 112. A method for fabricating asemiconductor component comprising: providing a substrate having a firstside, a second side and a substrate contact; forming a via in thesubstrate contact and the substrate to the second side; forming apolymer member on the substrate contact; and placing a wire in the via;and bonding the wire to the substrate contact with a loop portionthereof supported by the polymer member.
 113. The method of claim 112further comprising forming a contact on the loop portion.
 114. Themethod of claim 112 further comprising forming a metal layer on the loopportion configured to provide wear resistance or oxide penetration. 115.The method of claim 112 further comprising forming a polymer layer onthe first side leaving an outer surface of the loop portion exposed.116. The method of claim 112 further comprising forming a second contacton an end of the wire proximate to the second side.
 117. The method ofclaim 112 wherein the forming the polymer member step comprisesdepositing, molding or placing a polymer material on the substratecontact.
 118. The method of claim 112 wherein the placing and bondingsteps are performed using a bonding capillary.
 119. A method forfabricating a semiconductor component comprising: providing a substratehaving a first side, a second side and a substrate contact; forming avia in the substrate contact and the substrate to the second side;forming a polymer member on the substrate contact; placing a wire in thevia; bonding the wire to the substrate contact with a loop portionthereof supported by the polymer member; and forming a first contact onthe wire proximate to the first side and a second contact on the wireproximate to the second side.
 120. The method of claim 119 furthercomprising making a temporary electrical connection between the firstcontact and a test contact with the polymer member providing a biasingforce.
 121. The method of claim 119 further comprising making atemporary electrical connection between the second contact and a testcontact with the polymer member providing a biasing force.
 122. Themethod of claim 119 wherein the first contact comprises an outer surfaceof the loop portion.
 123. The method of claim 119 further comprisingmaking an electrical connection between the loop portion and anothercontact with the polymer member providing a biasing force.
 124. Themethod of claim 119 wherein the second contact comprises a ball contacton an end of the wire.
 125. The method of claim 119 wherein the formingthe polymer member step comprises depositing, molding or placing apolymer material on the substrate contact.
 126. The method of claim 119wherein the placing and bonding steps are performed using a bondingcapillary.
 127. The method of claim 119 further comprising forming anouter layer on the first contact configured to provide wear resistanceor oxide penetration.
 128. The method of claim 119 further comprisingforming an outer layer on the second contact configured to provide wearresistance or oxide penetration.
 129. The method of claim 119 furthercomprising forming a polymer layer on the first side substantiallyencapsulating the loop portion while leaving the first contact exposed.130. The method of claim 119 further comprising forming a polymer layeron the second side while leaving the second contact exposed.